202 Stainless Steel Sheet

Manufacturer and exporter of 202 Stainless Steel Sheet located in Mumbai, India available in various standards and grades such as ASTM A314/A276,AISI 202 Stainless Steel and UNS S20200 Stainless Steel Sheet, Grade 202 stainless steel is a type of Cr-Ni-Mn stainless with similar properties to A240/SUS 302 stainless steel. The toughness of grade 202 at low temperatures is excellent. It is one of the most widely used precipitation hardening grades, and possesses good corrosion resistance, toughness, high harness, and strength.

202 Stainless Steel Sheet Suppliers, ASTM A314/A276 202 Stainless Steel Sheet, UNS S20200 Stainless Steel Sheet, Exporters of Stainless Steel 202 Sheet, 202 stainless steel Sheet suppliers, AISI 202 stainless steel Sheet, stainless steel 202 ASTM A240 Sheet, Alloy 202 Austenitic Stainless Steel Sheet, Exporters Of ASTM A240 Stainless steel 202 Sheet

Chemical Composition :

The chemical composition of grade 202 stainless steel is outlined in the following table.

Element Content (%)
Iron, Fe 68
Chromium, Cr 17- 19
Manganese, Mn 7.50-10
Nickel, Ni 6-Apr
Silicon, Si <=1
Nitrogen, N <= 0.25
Carbon, C <= 0.15
Phosphorous, P <= 0.060
Sulfur, S <= 0.030

Mechanical Properties :

The mechanical properties of grade 202 stainless steel are displayed in the following table.

Properties Metric Imperial
Tensile strength 515 MPa 74694 psi
Yield strength 275 MPa 39900 psi
Elastic modulus 207 GPa 30000 ksi
Poisson's ratio 0.27-0.30 0.27-0.30
Elongation at break 40% 40%

Other Designations :

Equivalent materials to grade 202 stainless steel are given below.

ASTM A276 ASTM A314 ASTM A412 ASTM A429
ASTM A473 ASTM A666 FED QQ-S-763 FED QQ-S-766
FED STD-66 SAE 30202 SAE J405 (30202)  

Manufacturing Process :

The machinability of grade 202 stainless steel produces long, gummy chips. Machining can also be performed in the annealed condition. For heat treatment, the material has to be soaked at 1038°C (1900°F) for 30 min and cooled below 16°C (60°F) for full martensite transformation. The material can be welded by common fusion and resistance methods; however, this steel should not be joined using oxyacetylene welding method. The recommended filler metal is AWS E/ER630. Forging can be done by pre-soaking for 1 h at 1177°C (2150°F). Forging below 1010°C (1850°F) is not advisable.

Applications :

The grade 202 steel can be made into plates, sheets, and coils to be used in the following:

  • Restaurant equipment
  • Cooking utensils
  • Sinks
  • Automotive trim
  • Architectural applications such as windows and doors
  • Railway cars
  • Trailers
  • Hose clamps.

Jainex Steel and Metal exports ASTM A314, ASTM A276 202 Stainless Steel Sheet, Stainless Steel 202 Sheet, AISI 202 Sheet, SS S20200 Sheet to countries like Saudi Arabia, Bangladesh, United Arab Emirates, Brazil, Russia, Indonesia, Egypt, Iran, Kuwait, Taiwan, Oman, Qatar, South Africa, Australia, Pakistan, Malaysia.